Learning Forum

[Mansoureh]

hello every one,

I did my compression test on my model and i have my data form forece_displacement. after simulating in Ansys , i can only plot plasticity, but i cant access to fracture and can not plot the same curve as experimental.

I extract my plasticity data from a reference stress strain curve and change them to true data and used multilinear isotropic hardening to input them to Ansys.

how can i get the curve like experimental?

My material is Ti6Al4V and i attached my figure here, also my material that i defined as a new material in Ansys.

please guide me.

thanks in advance

[Ashish Khemka]

nnPlease see if the following posts look useful:nnnRegards,nAshish Khemkan

[Mansoureh]

Dear @akhemka,nThank you so much for answering me.nI saw this post before but you know my problem is this(I explain this below): nI put my samples under a compression test and my sample broke after several seconds under loading. This process gives me a force-displacement( the black line). My problem is about how to simulate fraction. If you see my figure that I uploaded above, in 8% strain sample broke and the force-displacement curve falls down. and some distortion and ups and down can be seen in this curve. I don't know how to make close my figure to the experimental one. nI can just simulate up to the plastic region and I do not know how to simulate the fracture section. Can you guide me on how can I don't that section in ansys?nShould I add sth related to fracture analysis to static structural analysis?.