[Niki Papachristou]

Hi Phat,

Thank you for reaching out to us! I think in this case you may turn TiO2 to semiconductor with some proper material properties: 

Tips for creating a new semiconductor material

As for the mesh issue, there might be different reasons for that to occur. One common one can be that after partitioning the simulation volume, there might be that some domains have no materials assigned. Please refer to this article: Partitioned volumes in finite element solvers - Simulation object

Let me know if these two suggestion worked, or if you have any additional question.

Kind Regards,

Niki